Influence of the Heat Treatment on the Microstructure and Corrosion Resistance of Austempered Ductile Iron (ADI)

Résumé

The influence of the hold time of the austempering heat treatment at 280°C on the microstructure and corrosion resistance in NaCl-based media of austempered ductile iron was investigated using X-ray diffraction, micro-hardness measurements, corrosion tests and surface observations. Martensite was only found in the sample which was heat treated for a short period (10 minutes). Corrosion tests revealed that this phase does not play any role in the anodic processes. Numerous small pits were observed in the α-phase which is the precursor sites in all samples (whatever the value of the hold time of the austempering heat treatment).

Domaines

Chimie
Fichier principal
Vignette du fichier
AMM-2020-1-18-Krawiec_20_12_2019.pdf (2.29 Mo) Télécharger le fichier
Origine : Fichiers éditeurs autorisés sur une archive ouverte

Dates et versions

hal-03024566 , version 1 (25-11-2020)

Identifiants

Citer

Halina Krawiec, Vincent Vignal, Janusz Lelito, A. Krystianiak, Tyrala E. Influence of the Heat Treatment on the Microstructure and Corrosion Resistance of Austempered Ductile Iron (ADI). Archives of Metallurgy and Materials, 2020, ⟨10.24425/amm.2019.131108⟩. ⟨hal-03024566⟩
21 Consultations
43 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More